The ability of a material to deform plastically without fracturing, is called ductility. In the materials usually machined in our shops, ductility is measured by determining the percent of elongation and the percent reduction of area on a specimen during a tensile test.
Our earlier post about Ductility showed how ductility can impact our shops. In this post, we will describe how we can measure ductility and use it to predict behavior based on values reported on certs and test reports.
The percent elongation and percent reduction of area values shown on our test reports and material certifications from our material suppliers indicate the ductility of the material tested.
In the tensile test, a cylindrical specimen is gripped securely and subjected to a uniaxial load and elongated until it breaks. At the end of the test, the pieces of the fractured specimen are fitted back together again and the change of length between the two gage marks put on the specimen before testing is determined. The change is then expressed as a percentage of the original gage length.
The percent reduction of area is determined by measuring the minimum diameter of the broken test specimen after the two pieces are fitted together and the difference is expressed as a percentage of the original cross sectional area prior to the test.
A minimum of 12% elongation is recommended for consistent, trouble free thread rolling applications.
Rolled threads are stronger, so having the ductility to thread roll is important. However, too much ductility makes it difficult to get the chip to separate by cutting.
Low ductility can be problematic for cold deformation manufacturing processes such as thread rolling, cold forming, swaging, staking and crimping.
This is the designer’s compromise: if it is good for cutting, it is probably not very good for rolling.
HSC online Graphic of test specimens