Why Tool Life Can Vary- Carbon and Alloy Steels

Tool life can vary when machining carbon and alloy steels despite the use of our best technology and our efforts to control our processes.

Many ways that tools can fail. this post discusses factors in the steel that can lead to this.

Many ways that tools can fail. This post discusses factors in the steel that can lead to this.

Here are 6 factors that can affect tool life in your shop.

  1. Variations between suppliers. Suppliers’ melt processes, scrap practices, melt recipes, and reduction in cold drawing and straightening practice can significantly affect the way that the chip breaks and resulting built up edge on tool and resulting surface finish. Even though the grade is the “same.”
  2. Variations in Chemistry.  A potential subset of variations between suppliers, the fact is that a plain carbon grade with 0.005 wt. % Sulfur  will not machine at all like the material with 0.025 wt% sulfur.
  3. Variations in grain size. While this factor is typically more relevant in stainless steels, when machining forgings, blocky structures resulting from excessive forging temperatures can result in inconsistent machining performance.
  4. Variations in microstructure. In this case, it is not so much about the grain size, as it is about the structure present. This is particularly problematic in the ~0.40 wt% carbon alloy grades like 4037.
  5. Decarburization or scaling on the work surface. Decarb can result is a carbon poor gummy surface, only to then transition into a fully carbon containing microstructure. Scale on the work surface can result in excessive tool wear, due to the very high hardnesses of the various iron oxides that may be present (Hematite, the red oxide of iron, Fe2O3, has a microhardness of approximately 1030 DPH.
  6. Deoxidation /High Inclusion Count. Free machining grades such as 12XX and 11XX steels are typically sold to a “Coarse Grain Practice” with no deliberate additions of grain refiners or deoxidizers. Sometimes, you may find deliberate additions of Silicon to 1144 in order to improve the internal soundness of the steel, the resulting silicates can abrade the edge of the tool when running at the surface feeds expected for a resulfurized steel. The addition of aluminum as a grain refiner can cause rapid edge wear as well. Rarely, very rarely, one might encounter exogenous inclusions entrapped in the steel from melt and casting. These can be real showstoppers.

Takeaway: Purchasing the same item from different suppliers hurls the full range of global variation at your machining operations. Standardizing on a single supplier for an item will allow you to get to steady state in your process.

Photo courtesy of via  CTE Magazine Plus

 

Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s